Singh, K. and Negi, N. S. and Kotnala, R. K. and Singh, M. (2008) Dielectric and magnetic properties of (BiFeO3)1−x(PbTiO3)x ferromagnetoelectric system. Solid State Communications, 148 (1-2). pp. 18-21. ISSN 0038-1098

PDF - Published Version Restricted to Registered users only Download (1229Kb) | Request a copy

Abstract

BiFeO3–PbTiO3(BFPTO) ferromagnetoelectric (FME) material, with improved resistivity (∼109View the MathML source cm) and high relative density (∼0.95) is successfully prepared by sol-gel method. The microstructures, dielectric and magnetic properties are investigated by mean of X-rays diffraction, Scanning electron microscope, impedance analyzer and Vibrating sample magnetometer. A well crystalline powder was obtained after annealing in air at 825 ∘C for 20 min. The average particle size of sample calcined at 825 ∘C is 1–2 μm. Structural transformation from rhombohedral (x=0.0) to tetragonal (x=0.3) has been revealed from XRD analysis. Dielectric constant and resistivity of BFPTO is found to be increase as the content of PbTiO3 (PTO) increase and tangent loss are reduced by increasing the content of PTO in BFPTO composites. The study of M–H curve reveals that BiFeO3 (BFO) is antiferromagnetic with small residual magnetism (0.012 emu/g) due to canting of the spin. For composites with x=0.1 and 0.3, a large induced magnetization was observed than that of BiFeO3 single Crystal. Hence BFPTO prepared in study can be leads to ferromagnetic state that has remanent magnetization, unlike that of the earlier reported BiFeO3.

Item Type:	Article
Additional Information:	Copyright for this article belongs to M/S Elsevier B.V.
Uncontrolled Keywords:	Multiferroic; B. Sol-gel; D. Magnetic properties; D. Dielectric constant
Subjects:	Physics
Divisions:	UNSPECIFIED
Depositing User:	Ms Neetu Chandra
Date Deposited:	09 Apr 2013 09:31
Last Modified:	09 Apr 2013 09:31
URI:	http://npl.csircentral.net/id/eprint/975

Actions (login required)

View Item