Gope, Jhuma and Kumar, Sushil and Parashar, A. and Dixit, P. N. and Rauthan, C. M. S. and Panwar, O. S. and Patel, D. N. and Agarwal, S. C. (2009) Amorphous and nanocrystalline silicon made by varying deposition pressure in PECVD process. Journal of Non-Crystalline Solids, 355 (45-47). pp. 2228-2232. ISSN 0022-3093

[img] PDF - Published Version
Restricted to Registered users only

Download (341Kb) | Request a copy

Abstract

Silicon thin films are deposited using plasma enhanced chemical vapor deposition (PECVD) of silane, argon, hydrogen mixture at various pressures in the range of 2–8 Torr. Raman scattering shows these to be amorphous in the pressure range 6–8 Torr, and nanocrystalline in the range 2–4 Torr. The volume fraction of nanocrystals is estimated by fitting the Raman data to three peaks and is found to be ∼75% for the films deposited at low pressure, density of states of these films was measured. It is observed that the electrical conduction in these films depends on the crystalline volume fraction (ρ), estimated from the laser Raman Spectroscopy. Temperature dependence electrical conductivity shows that at lower temperatures thermionic emission dominates for the films with lower ρ, whereas, hopping is the main conduction mechanism for the films having high ρ. The density of states is estimated from the space charge limited currents (SCLC) observed at high fields. Photoconductivity at room temperature is also measured. The amorphous films are found to be more photosensitive than the nanocrystalline one. In the context of these findings, changes in the properties of silicon from amorphous to nanocrystalline are described.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s Elsevier B.V.
Uncontrolled Keywords: Amorphous semiconductors; Silicon; Nanocrystalline materials
Subjects: Materials Science
Divisions: UNSPECIFIED
Depositing User: Ms Neetu Chandra
Date Deposited: 13 Aug 2012 07:23
Last Modified: 13 Aug 2012 07:23
URI: http://npl.csircentral.net/id/eprint/400

Actions (login required)

View Item View Item