Bahadur, Nupur and Pasricha, Renu and -, Govind and Chand, Suresh and Kotnala, Ravinder Kumar (2012) Effect of Ni doping on the microstructure and high Curie temperature ferromagnetism in sol-gel derived titania powders. Materials Chemistry and Physics, 133 (1). 471-479. ISSN 0254-0584

[img] PDF - Published Version
Restricted to Registered users only

Download (1315Kb) | Request a copy

Abstract

Undoped, 0.05 and 0.5 mol% Ni-doped TiO2 powders were prepared by a modified sol-gel route. The doping effects on the microstructure and magnetism for the powdered samples have been systematically investigated. Doping of Ni in TiO2 inhibited rutile crystal growth. The probable reason for this is discussed on the basis of band calculation based analysis of electronic structures of 3d transition metal-doped TiO2 and the energetic, transformation kinetics and phase stability of anatase over rutile as the function of particle size. Room temperature ferromagnetism (RTFM) with the saturation magnetization of 12 m emu g(-1) and Curie temperature as high as 820K is observed only in case of 0.05 mol% Ni:TiO2 powdered sample, whereas undoped TiO2 was diamagnetic and 0.5 mol% Ni:TiO2 was paramagnetic in nature. The role of any magnetic impurity or any Ni metal in the origin of the RTFM has been ruled out by energy dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) and high resolution TEM (HRTEM) analysis, whereas magnetic force microscopy (MFM) established the presence of magnetic domains, supporting the intrinsic diluted magnetic semiconductor behavior. The observed ferromagnetism has been attributed to the spin ordering through exchange interaction between holes trapped in oxygen orbitals adjacent to Ni substitutional sites.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s Elsevier.
Subjects: Materials Science
Divisions: UNSPECIFIED
Depositing User: Users 27 not found.
Date Deposited: 20 Feb 2020 08:33
Last Modified: 20 Feb 2020 08:33
URI: http://npl.csircentral.net/id/eprint/3622

Actions (login required)

View Item View Item