Baronia, Richa and Goel, Jyoti and Tiwari, Shraddha and Singh, Priti and Singh, Dinesh and Singh, Surinder P. (2017) Efficient electro-oxidation of methanol using PtCo nanocatalysts supported reduced graphene oxide matrix as anode for DMFC. International Journal of Hydrogen Energy, 42. pp. 10238-10247. ISSN 0360-3199

PDF - Published Version Restricted to Registered users only Download (1865Kb) | Request a copy

Abstract

Platinum - cobalt (PtCo) alloy based highly efficient nano electro-catalysts on reduced graphene oxide (rGO) matrix have been synthesized for the electro-oxidation of methanol, by chemical reduction method. Different molar ratio of Pt (IV) and Co (II) ions along with graphene oxide (GO) were reduced using ethylene glycol to obtain PtCo nanoparticles onto rGO sheets (Pt/rGO, PtCo (1:1)/rGO, PtCo (1:5)/rGO, PtCo (1:9)/rGO and PtCo (1:11)/rGO) with 20 wt. % metal and 80 wt. % rGO. The average particle size of PtCo nanoparticles onto rGO support was observed to be 2-5 nm using XRD and TEM analysis. The PtCo (1:9)/rGO nanocomposite catalyst exhibited similar to 23 times higher anodic current density compare to commercially available Pt/C catalyst (1.68 mA/cm(2)) for methanol oxidation reaction. The peak power density of 118.4 mW/cm(2) was obtained for PtCo (1:9)/rGO catalyst in direct methanol fuel cell (DMFC) at 100 degrees C, 1 bar, and 2 M methanol as anode feed, which is similar to 3 times higher than that of Pt/C catalyst. The results indicate the potential application of synthesized nanocomposite catalyst in commercial DMFCs.

Item Type:	Article
Additional Information:	Copyright for this article belongs to M/s Elsevier.
Subjects:	Chemistry > Physical Chemistry Electrochemistry Energy Fuels
Divisions:	UNSPECIFIED
Depositing User:	Users 27 not found.
Date Deposited:	06 Sep 2018 06:51
Last Modified:	06 Sep 2018 06:51
URI:	http://npl.csircentral.net/id/eprint/2680

Actions (login required)

View Item