Sharma, Sunil Dutta and Singh, Davinder and Saini, K. K and Kant, Chander and Sharma, Vikash and Jain, S. C. and Sharma, C. P. (2006) Sol-gel-derived super-hydrophilic nickel doped TiO2 film as active photo-catalyst. Applied Catalysis A: General, 314. pp. 40-46. ISSN 0926-860X

PDF - Published Version Restricted to Registered users only Download (345Kb) | Request a copy

Abstract

Pure and nickel doped TiO2 thin films on soda glass substrates were prepared by sol-gel dip coating process. The resulting films were annealed at 500 degrees C for 1 h and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and UV-vis-near IR techniques. AFM reveals that doping of Ni ions suppresses the grain growth of crystal in the TiO2 film. The contact angle with water of these films was measured by sessile drop method. The undoped films could be entirely wetted by water after 1 h UV illuminations, while 0.5 mol% Ni ion-doped films become entirely wetted after 20 min UV illumination. The photo-catalytic activity was characterized by photocatalytic degradation of aqueous methyl orange under UV radiation. It is found that, with a suitable amount (2-10 mol%), the Ni dopant increases the photo-catalytic activity of TiO2 films. The mechanism can be attributed to these processes: (1) as the anatase grain sizes decrease with Ni doping and the specific surface areas of doped TiO2 films increase, the charge transfer in TiO2 film is promoted; (2) by enhancing the electron-hole pair separation and inhibiting their recombination, the Ni dopant enhances the charge pair separation efficiency for doped TiO2 films

Item Type:	Article
Additional Information:	Copyright for this article belongs to M/s Elsevier.
Subjects:	Physical Chemistry/Chemical Physics
Divisions:	UNSPECIFIED
Depositing User:	Users 27 not found.
Date Deposited:	07 Aug 2018 08:06
Last Modified:	07 Aug 2018 08:06
URI:	http://npl.csircentral.net/id/eprint/2550

Actions (login required)

View Item