Porwal, Rajni and Gupta, Anurag and Budhani, R. C. (2016) Crossover from magnetostatic to exchange coupling in La0.67Ca0.33MnO3/YBa2Cu3O7/La0.67Ca0.33MnO3 heterostructures. Journal of Physics: Condensed Matter, 28 (50). ISSN 0953-8984

PDF Restricted to Registered users only Download (2624Kb) | Request a copy

Abstract

The influence of YBa2Cu3O7 (YBCO) superconductor layer (S-layer) with a varying thickness d(YBCO) = 20-50 nm on the magnetic coupling between two La0.67Ca0.33MnO3 (LCMO) ferromagnet layers (F-layer, thickness d(LCMO) = 50 nm) in F/S/F heterostructures (HSs) was investigated by measuring global magnetization (M) in a temperature (T) range = 2-300 K and a magnetic field (H) range = 0-10 kOe. All the HSs were superconducting with the critical temperature (TC) decreasing from = 78 to 36 K with decrease in d(YBCO), whereas the ferromagnetic ordering temperature T-M = 250 K did not change much. Systematically measured M-H loops of all HSs at both T > T-C and T < T-C show three main results (a) the two step magnetic reversal above T-C converts into a four step reversal below T-C in HSs with d(YBCO) >= 30 nm, (b) the magnitude and magnetic field corresponding to the additional two switching steps show characteristic evolution with T and d(YBCO); and (c) the HS with d(YBCO) = 20 nm shows radically different behaviour, where the two step magnetic reversal above T-C continues to persist below T-C and converts into a single step reversal at T << T-C. The first two results indicate magnetostatic coupling between the magnetic domains and the vortices across the two F/S interfaces resulting in reversal dynamics different from that deep within the LCMO layers. Whereas, the result 'c' reveals indirect exchange coupling between LCMO layers through the superconducting YBCO layer, which is a clear experimental evidence of coexistence of ferromagnetism and superconductivity in nm scale F/S/F HSs expected theoretically by Sa de Melo (2003 Physica C 387 17-25).

Item Type:	Article
Additional Information:	Copyright for this article belongs to M/s IOP Publishing.
Uncontrolled Keywords:	cuprate-manganite heterostructure, magnetization, superconductivity, magnetic coupling, thin film
Subjects:	Applied Physics/Condensed Matter
Divisions:	UNSPECIFIED
Depositing User:	Dr. Rajpal Walke
Date Deposited:	16 Nov 2017 08:53
Last Modified:	16 Nov 2017 08:53
URI:	http://npl.csircentral.net/id/eprint/2171

Actions (login required)

View Item