Mudgel, Monika and Awana, V. P. S. and Bhalla, G. L. and Kishan, H. (2008) Superconductivity of non-stoichiometric intermetallic compound NbB2. Solid State Communications, 147 (11-12). 439-442 . ISSN 0038-1098
PDF
- Published Version
Restricted to Registered users only Download (2145Kb) | Request a copy |
Abstract
We report the synthesis, magnetic susceptibility and crystal structure analysis for NbB2+x (X = 0.0-1.0) samples. The study helps find a correlation among the lattice parameters, chemical composition and the superconducting transition temperature T-c. Rietveld analysis is done on the X-ray diffraction patterns of all synthesized samples to determine the lattice parameters. The a parameter decreases slightly and has a random variation with increasing x, while c parameter increases from 3.26 for pure NbB2 to 3.32 for x = 0.4 i.e. NbB2.4. With higher Boron content (x > 0.4) the c parameter decreases slightly. The stretching of lattice in c direction induces superconductivity in the non-stoichiometric niobium boride. Pure NbB2 is non-superconductor while the other NbB2+x (x > 0.0) samples show diamagnetic signal in the temperature range 8.9-11 K. Magnetization measurements (M-H) at a fixed temperature of 5 K are also carried out in both increasing and decreasing directions of field. The estimated lower and upper critical fields (H-c1 & H-c2) as viewed from M-H plots are around 590 and 2000 Oe, respectively, for NbB2.6 samples. In our case, superconductivity is achieved in NbB2 by varying the Nb/B ratios, rather than changing the processing conditions as reported by others.
Item Type: | Article |
---|---|
Additional Information: | Copyright for this article belongs to M/s Elsevier. |
Subjects: | Applied Physics/Condensed Matter |
Divisions: | UNSPECIFIED |
Depositing User: | Ms Neetu Chandra |
Date Deposited: | 18 Apr 2017 11:01 |
Last Modified: | 18 Apr 2017 11:01 |
URI: | http://npl.csircentral.net/id/eprint/2120 |
Actions (login required)
View Item |