Dhayal, Marshal and Cho, Su-In and Moon, Jun Young and Cho, Su-Jin and Zykova, Anna (2008) S180 cell growth on low ion energy plasma treated TiO2 thin films. Applied Surface Science, 254 (11). pp. 3331-3338. ISSN 0169-4332

[img] PDF - Published Version
Restricted to Registered users only

Download (1517Kb) | Request a copy

Abstract

X-ray photoelectron spectroscopy (XPS) was used to characterise the effects of low energy (<2 eV) argon ion plasma surface modification of TiO2 thin films deposited by radio frequency (RF) magnetron sputter system. The low energy argon ion plasma surface modification of TiO2 in a two-stage hybrid system had increased the proportion of surface states of TiO2 as Ti3+. The proportion of carbon atoms as alcohol/ether (Csingle bondOX) was decreased with increase the RF power and carbon atoms as carbonyl (Cdouble bond; length as m-dashO) functionality had increased for low RF power treatment. The proportion of C(double bond; length as m-dashO)OX functionality at the surface was decreased at low power and further increase in power has showed an increase in its relive proportion at the surface. The growth of S180 cells was observed and it seems that cells are uniformly spreads on tissue culture polystyrene surface and untreated TiO2 surfaces whereas small-localised cell free area can be seen on plasma treated TiO2 surfaces which may be due to decrease in C(double bond; length as m-dashO)OX, increase in Cdouble bond; length as m-dashO and active sites at the surface. A relatively large variation in the surface functionalities with no change in the surface roughness was achieved by different RF plasma treatments of TiO2 surface whereas no significant change in S180 cell growth with different plasma treatments. This may be because cell growth on TiO2 was mainly influenced by nano-surface characteristics of oxide films rather than surface chemistry.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s Elsevier B.V.
Subjects: Chemistry
Materials Science
Applied Physics/Condensed Matter
Divisions: UNSPECIFIED
Depositing User: Ms Neetu Chandra
Date Deposited: 05 Apr 2017 11:29
Last Modified: 05 Apr 2017 11:29
URI: http://npl.csircentral.net/id/eprint/2082

Actions (login required)

View Item View Item