Yadav, Kamlesh and Singh, M. P. and Singh, H. K. and Razavi, F. S. and Varma, G. D. (2012) Magnetic and charge ordering properties of Bi0.6-x(RE)(x)Ca0.4MnO3 (0.0 <= x <= 0.6) perovskite manganites. Journal of Applied Physics , 111 (7). 07E128-07E131. ISSN 0021-8979

[img] PDF - Published Version
Restricted to Registered users only

Download (980Kb) | Request a copy

Abstract

In this work, we studied structural, magnetic, and charge ordering properties of polycrystalline Bi0.6-x (RE)(x) Ca0.4MnO3 (x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, and 0.6) samples, synthesized via solid state reaction route and by taking RE = La, Pr, and Nd, separately. The temperature dependence magnetization measurement reveals that the x = 0.0 compound (BCMO) exhibits a charge ordered (CO) and antiferromagnetic (AFM) phase with the charge ordering temperature (T-CO) similar to 289 K and the antiferromagnetic ordering temperature (T-N) similar to 136 K. Only a small fraction of La-dopant in BCMO is sufficient to destroy the CO completely, whereas a large concentration of La (viz., x = 0.2 to x = 0.6) promotes ultimately a paramagnetic to ferromagnetic (PM-FM) transition, and the PM-FM transition temperature (T-C) decreases progressively from 241 K to 203 K as x increases from 0.2 to 0.5. In contrast, systematic substitution of Pr or Nd at Bi site induces an intriguing interplay between the charge ordering and antiferromagnetism. Our results demonstrate that the value of T-CO decreases with increasing value of "x" and the value of T-N increases sharply at both the extremes; however, it remains nearly constant from x 0.2 to 0.4. In our samples, a glassy magnetic states are also observed at far below the T-N.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s American Institute of Physics.
Subjects: Applied Physics/Condensed Matter
Divisions: UNSPECIFIED
Depositing User: Users 27 not found.
Date Deposited: 13 Mar 2020 11:30
Last Modified: 13 Mar 2020 11:30
URI: http://npl.csircentral.net/id/eprint/3508

Actions (login required)

View Item View Item