Kumar, Virendra and Gaur, Anurag and Sharma, Neha and Shah, Jyoti and Kotnala, R. K. (2013) High temperature dielectric and magnetic response of Ti and Pr doped BiFeO3 ceramics. Journal of Alloys and Compounds, 39 (7). pp. 8113-8121. ISSN 0925-8388

[img] PDF - Published Version
Restricted to Registered users only

Download (5Mb) | Request a copy

Abstract

In the present study, four different compositions of Ti and Pr doped BiFeO3 samples were synthesized by conventional rapid liquid phase sintering and their structural, dielectric, ferroelectric and magnetic properties were investigated. High temperature dielectric study shows different anomalous response for all compositions. A major peak in dielectric constant versus temperature curve is observed at 640 K for pristine BiFeO3 which shifts to 545 K for Ti doped (BiFe0.9Ti0.1O3) sample. Moreover, multiple peaks are observed for Pr doped (Bi0.9Pr0.1FeO3) sample in temperature range of 400-800K. The room temperature P E loop study shows that the value of maximum polarization increases from 0.185 to 0.859 mu C/cm(2) for Pr doped (Bi0.9Pr0.1FeO3) sample and also increases the ability of BiFeO3 to withstand higher electric field. Room temperature magnetic (M R) curve shows a slight increment in the value of magnetization from 0.071 to 0.078 emu/gm for pristine BiFeO3 to Pr and Ti co-doped Bi0.9Pr0.1Fe0.9Ti0.1O3, respectively.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s Elsevier.
Subjects: Materials Science
Divisions: UNSPECIFIED
Depositing User: Users 27 not found.
Date Deposited: 09 Nov 2021 10:01
Last Modified: 09 Nov 2021 10:01
URI: http://npl.csircentral.net/id/eprint/3192

Actions (login required)

View Item View Item