Hashim, Mohd and -, Alimuddin and Shirsath, Sagar E. and Kumar, Shalendra and Kumar, Ravi and Roy, Aashis S. and Shah, Jyoti and Kotnala, R. K. (2013) Preparation and characterization chemistry of nano-crystalline Ni-Cu-Zn ferrite. Journal of Alloys and Compounds, 549. pp. 348-357. ISSN 0925-8388
PDF
- Published Version
Restricted to Registered users only Download (1513Kb) | Request a copy |
Abstract
In submitted research; nanocrystalline powders having elements Ni0.5Cu0.25Zn0.25Fe2 xInxO4 with varied amounts of indium ( x = 0.0, 0.1, 0.2, 0.3 and 0.4) were grown-up by modified citrate to nitrate alchemy. The realism of single phase cubic spinel creation of the synthesized ferrite samples was studied by the DTA-TGA, XRD, SEM, EDX, FT-IR, VSM and dielectric measurements. SEM was applied to inspect the morphological variations and EDX was used to determine the compositional mass ratios. The studies on the dielectric constant (epsilon'), dielectric loss (epsilon ''), loss tangent (tan delta), ac conductivity (sigma(ac)), resistive and reactive parts of the impedance analysis (Z' and Z '') at room temperature were also carried out. The saturation magnetizations (Ms) were determined using the vibrating sample magnetometer (VSM). Ms. decreased with the increase In3+ doping content, as Fe3+ of 5(mu B) ions are replaced by In3+ of 5 mu(B) ions.
Item Type: | Article |
---|---|
Additional Information: | Copyright for this article belongs to M/s Elsevier. |
Subjects: | Chemistry > Physical Chemistry Materials Science Metallurgy & Metallurgical Engineering |
Divisions: | UNSPECIFIED |
Depositing User: | Users 27 not found. |
Date Deposited: | 03 Jul 2020 10:57 |
Last Modified: | 03 Jul 2020 10:57 |
URI: | http://npl.csircentral.net/id/eprint/3089 |
Actions (login required)
View Item |