Kumar, Anoop S. and Bhandari, Hema and Sharma, Chandrica and Khatoon, Fehmeeda and Dhawan, Sundeep K. (2013) A new smart coating of polyaniline-SiO2 composite for protection of mild steel against corrosion in strong acidic medium. Polymer International , 62. pp. 1192-1201. ISSN 0959-8103

[img] PDF - Published Version
Restricted to Registered users only

Download (521Kb) | Request a copy

Abstract

Organic coating approaches for corrosion protection with inherently conducting polymers have become important because of restriction on the use of heavy metals and chromates in coatings due to their environmental problems. The present work is directed towards the synthesis of polyaniline (PANI) and polyaniline-SiO2 composites (PSCs) by chemical oxidation polymerization in the presence of phosphoric acid and evaluation of synthesized PANI and PSCs for protection of mild steel from corrosion in a strong aggressive medium (i.e. 1.0 mol L-1 HCI). A suitable coating with PSC was formed on mild steel using epoxy resin by the powder coating technique. A comparative study of the corrosion protection efficiency of mild steel coated with PANI and PSC in 1.0 mol L-1 HCI solution was evaluated using the Tafel extrapolation, chrono-amperometry and weight loss methods. The PSC coating showed that a significant reduction in the corrosion current density reflects the better protection of mild steel in an acidic environment. Higher protection efficiency up to 99% was achieved by using PSC-coated mild steel at 6.0 wt% loading of PSC in epoxy resin. The coating performance and corrosion rate of mild steel were investigated by using immersion of polymer-coated mild steel in 1.0 mol L-1 HCI for 60 days and indicated that PSC-coated mild steel showed better performance from corrosion than PANI in an acidic medium.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s Wiley-Blackwell.
Subjects: Polymer Science
Divisions: UNSPECIFIED
Depositing User: Users 27 not found.
Date Deposited: 28 May 2020 10:20
Last Modified: 28 May 2020 10:20
URI: http://npl.csircentral.net/id/eprint/2968

Actions (login required)

View Item View Item