Kumar, Pawan and Gaur, Anurag and Kotnala, R. K. (2017) Magneto-electric response in Pb substituted M-type barium-hexaferrite. Ceramics International, 43. pp. 1180-1185. ISSN 0272-8842

[img] PDF - Published Version
Restricted to Registered users only

Download (1295Kb) | Request a copy

Abstract

Pb-substituted barium hexaferrite with chemical formula, Ba1-xPbxFe12O19 (x=0.0, 0.1, 0.2, 0.3, 0.4) were prepared by co-precipitation method and citric acid was used as the organic precipitating agent. The samples were characterized by X-ray (XRD), scanning electron microscopy (SEM), Polarization versus Electric field (PE) loop tracers and vibrating sample magnetometer (VSM). XRD analysis confirms the single hexagonal phase formation for all the compounds and indicates that all Pb ions are situated into the lattice of barium ferrite. Images of scanning electron microscopy show that the grains are regular and well defined structures. P-E loops shows that the value of remnant polarization and saturation polarization increases up to x=0.2 and then decreases with increasing the Pb doping contents. Magnetization versus field (M-H) curves shows that the coercivity first increases and then decreases with the increase in Pb content with maximum value of coercivity (1270.38 Gauss) for x=0.2 sample. Magnetoelectric quadratic coefficient beta has been measured by the dynamic magnetoelectric method at room temperature. The maximum value of magneto-electric coupling coefficient is 5.27x10(-4) mu V/cm-Oe(2) at 3500 Oe for x=0.3 sample.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s Elsevier.
Subjects: Materials Science
Divisions: UNSPECIFIED
Depositing User: Users 27 not found.
Date Deposited: 12 Nov 2018 07:17
Last Modified: 12 Nov 2018 07:17
URI: http://npl.csircentral.net/id/eprint/2784

Actions (login required)

View Item View Item