Kaswan, Kavita and Agarwal, Ashish and Sanghi, Sujata and Kotnala, R. K. (2016) Crystal structure refinement and magnetic properties of Bi0.8Ba0.2FeO3 substituted Na0.5Bi0.5TiO3 ceramics. Journal of Molecular Structure, 1108. pp. 54-59. ISSN 0022-2860

[img] PDF - Published Version
Restricted to Registered users only

Download (1297Kb) | Request a copy

Abstract

In this study, Bi0.8Ba0.2FeO3 modified Na0.5Bi0.5TiO3 ceramics having composition (1 - x)(Na0.5Bi0.5TiO3) - x(Bi0.8Ba0.2FeO3) with 0 <= x <= 0.40 are fabricated by conventional solid state reaction technique. Rietveld analysis of X-ray diffraction pattern of the prepared ceramics revealed that all the samples crystallized into single phase with rhombohedral symmetry (R3c space group). Magnetic measurements were performed at room temperature up to a field of 6 kOe. The magnetic hysteresis loops for samples x <= 0.10 show linear magnetic field dependence of magnetization with narrow hysteresis loop, indicating the typical antiferromagnetic nature (AFM) with canted spins. For samples 0.20 <= x <= 0.40, an appreciable increase in the values of remnant magnetization and coercive field are observed. Thus, the addition of BBFO content gives rise to significant increase in magnetization.

Item Type: Article
Additional Information: Copyright for this article belongs to M/s Elsevier.
Uncontrolled Keywords: X-ray crystallography Crystal structure Multiferroics Magnetic properties
Subjects: Chemistry > Physical Chemistry
Divisions: UNSPECIFIED
Depositing User: Dr. Rajpal Walke
Date Deposited: 16 Nov 2017 11:19
Last Modified: 16 Nov 2017 11:19
URI: http://npl.csircentral.net/id/eprint/2172

Actions (login required)

View Item View Item