Synthesis of CeO2 microcrystals fabricated on biaxially textured Ni-W substrate by using an e-beam evaporation technique.
The journal of the Korean Physical Society, 66 (5).
726-729 .
ISSN 0374-4884
Abstract
Cerium-oxide (CeO2) microcrystals have been synthesized on a biaxially textured Ni-5%W (200) substrate by using the Electron beam (e-beam) evaporation technique with CeO2 powder as the source material. The substrate temperature and electron beam gun power at which the microcrystals were formed were 400A degrees C and 400 W, respectively. The X-ray diffraction (XRD) analysis confirmed the crystallinity and a (111) orientation of the CeO2 crystals. Scanning electron microscope (SEM) image showed that the CeO2 crystals had large lateral dimensions in the range from 0.5 to 2.0 mu m. The Raman spectrum shows only one peak at 464 cm(-1) corresponding to the of F-2g mode of the CeO2 crystals. No reports are available on the preparation of CeO2 crystals with such a large size on textured Ni-W substrate by using e-beam evaporation technique.
Item Type: |
Article
|
Uncontrolled Keywords: |
E-beam evaporation,
CeO2 crystals,
X-ray diffraction,
Scanning electron microscopy,
Raman
spectra |
Subjects: |
Physics |
Divisions: |
UNSPECIFIED |
Depositing User: |
Dr. Rajpal Walke
|
Date Deposited: |
02 Dec 2016 07:43 |
Last Modified: |
02 Dec 2016 07:43 |
URI: |
http://npl.csircentral.net/id/eprint/2032 |
Actions (login required)
|
View Item |